Fine particle, high-tint, weather-stable yellow iron oxide pigment — ideal for plastics, coatings, inks and construction applications.
Micronized Iron Oxide Yellow 920M is from yellowish red power to bluish red power pigment.They own much fine particle size,more bright color,superior dispersibility,better color consistency,excellent resistance to color change and higher tinting strength.
Masterbatches, PVC, PE, PP — uniform dispersion and good heat stability during processing.
Architectural and industrial coatings with strong lightfastness and opacity.
Suitable for solvent and water-based inks with good rheology control.
Concrete coloring, pavers, and decorative concrete where long-term color retention is required.
Stable under vulcanization temperatures and does not bleed in adhesives.
| Density(g/cm3) | 5.2 |
| Appearance | Yellow power |
| Content of Fe2O3 % | 96 min |
| PH Value | 4.5-7.5 |
| Oil Absorption | 25-35 |
| Residue on 320 mesh,% | 0.008 max |
| Water soluble, % | 0.5 max |
| Volatile at 105 degree | 0.5 max |
| Tinting strength, % | 98-102 |
Available in 25 kg bags, 500 kg big bags, or bulk. Store in a cool, dry place; protect from humidity and contamination.
For best results, pre-disperse pigment in a suitable carrier with high-shear milling for masterbatch or paint systems. Use recommended dispersants and follow standard milling time profiles for micronized pigments to reduce agglomerates.
Note: The data contained here are based on our current knowledge and experience. It is the responsibility of user to test our products before the final application.