Micronized Iron Oxide Red 130M is from yellowish red power to bluish red power pigment.They own much fine particle size,more bright color,superior dispersibility,better color consistency,excellent resistance to color change and higher tinting strength.
micronized iron oxide red is widely used in coil coatings,corrosion protection,decorative paintings,plastic products,colored plastics,master batches,power coatings,emulsion paintings,flooring,industrial coatings,paints and coatings,plastic coatings,roof tile coating,wood plastic composites,printing inks,papers.
Note: The data contained here are based on our current knowledge and experience. It is the responsibility of user to test our products before the final application.
| Density(g/cm3) | 5.1-5.3 |
| Appearance | Red powder |
| Content of Fe2O3 % | 96 min |
| PH Value | 4.5-7.5 |
| Oil Absorption | 15-25 |
| Residue on 320 mesh,% | 0.008 max |
| Water soluble, % | 0.5 max |
| Volatile at 105 degree | 0.5 max |
| Tinting strength, % | 98-102 |
"Micronized" refers to pigment particles that have been finely milled to a very small particle size distribution. This improves dispersion, leads to smoother surface appearance, higher tinting efficiency and more uniform color in final formulations.
Typical industries include coatings & paints, plastics & masterbatch, printing inks, textiles and leather. It is formulated to perform across a wide range of binder and polymer systems.
For best results start with pre-dispersion in a compatible vehicle followed by high-shear milling or masterbatching. Exact processing depends on your formulation; request our technical data sheet for recommended recipes.
Micronized Iron Oxide Red 130M offers good lightfastness and weather resistance compared with organic reds, making it a strong choice for outdoor coatings and durable plastic applications.